Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1 Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9 Al–1 Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively.The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.     

Microstructure,mechanical properties and wear resistance of an Al–Mg–Si alloy produced by equal channel angular pressing

Microstructure, mechanical properties and wear resistance in an ultrafine-grained Al–Mg–Si alloy fabricated utilizing a combination of equal channel angular pressing (ECAP) and dynamic aging were investigated in this paper. The results indicated that the grain size of the ECAP alloy was significantly refined, i.e., to ~239 nm after three ECAP passes. Meanwhile, the yield and tensile strength of the ECAPed material reached 340 MPa and 445 MPa, respectively, while maintaining a significant uniform elongation of 14%. Wear resistance results demonstrated that the wear rate, wear depth and width of the ECAPed material decreased in comparison with the solution-treated (SST) and peak-aged (T6) conditions under a load range of 5–25 N. The adhesive wear that occurs in the undeformed specimens at 10 N does not appear in the ECAPed specimen at the same load, indicating that the ECAPed specimen delay the appearance of more serious wear mechanisms under certain loads. The cooperative interaction of high density nano-scale β" precipitates and dislocations resulted in a combination of super-high strength and good work hardening ability which suppressed the extension of cracks between the friction layer and the plastic deformation zone. As a consequence, the combination of ECAP and dynamic aging brings a significant improvement for antifriction performance of the 6061 aluminum alloy.     

ZrO2基固体电解质氧传感器的研究现状及发展趋势

近年来,由于ZrO2基固体电解质氧传感器具有高的测氧灵敏度和在高温下的化学稳定性,因而在节约能源、环境保护等方面得到了广泛的应用。该文首先介绍了ZrO2基固体电解质氧传感器的测氧原理,然后阐述了ZrO2基固体电解质氧传感器的研究现状;重点介绍了氧传感器导电理论,及在高温和低温条件下工作的氧传感器研究状况和氧传感器的应用研究,并对氧传感器未来的发展进行了分析和展望,指出为了获得高性能的氧传感器应重点发展纳米材料氧传感器。     

铝合金加工用刀具的使用研究（三）

当前我国各机械加工生产厂家引进国外进口设备及生产线较多，实现引进设备及生产线上刀具的国产化以降低生产成本，成为当前国内整个机械加工领域亟待解决的问题。     

EJK951型油水界面传感器在油田中的应用

结合生产实际 ,从不同角度分析了油田生产中油水界面的特性 ,简要介绍了EJK95 1型油水界面传感器的工作原理、特点及在油田生产中的应用情况 ,该表是基于传统的电容式传感器原理 ,结合现代微电子技术而研制生产的一种新型油水界面传感器 ,具有结构简单、测量精度高、稳定性好等特点 ,是油水界面测量中的优选仪表。①     

Influence of Microstructure and Sintering Routes on Transport Properties of Apatite Materials for Fuel Cells

1 Results Oxy-apatite materials are thought as zirconia-substitutes in Solid Oxide Fuel Cells due to their fast ionic conduction. However, the well known difficulties related to their densification prevent them from being used as such. This study presents strategies to obtain oxy-apatite dense materials and the influence of elaboration route on transport properties. Particular emphasis is put on the microstructure effect on ion conduction. By the combined use of freeze-drying and conventional or spark p...     

电磁相分离法制备自生表层复合材料

采用电磁相分离法制备出以初生富铁相（AlSiFeMn复杂金属间化合物）为增强相，表层硬度为HB62．25，基体硬度为HB59．00的Al-11.70%Si-1.20?-1.50%Mn合金自生表层复合材料，增强相的显微硬度为HV 842。87，大小为20－80μm，该表层复合材料同基体材料相比，耐磨性提高了57．41％，所用方法工艺过程简单，成本低，为解决材料在服役环境中不同部位，不同性能的问题提供了新途径。     

电荷守恒与磁链守恒定律的论证

本文对电荷守恒定律和磁链守恒定律从数学方面作了较深入的论证,并给出了其物理意义。     

Fe_3Al的抗高温氧化和耐热腐蚀性能

在７００℃与８５０℃的高温下，Ｆｅ＿３Ａｌ金属间化合物表面形成了Ａｌ＿２Ｏ＿３保护膜，使其抗氧化性能远优于不妨钢，２％Ｃｒ（原子百分比）加入Ｆｅ＿３Ａｌ会导致氧化过程初期氧化速率的增高，在熔融的硫酸盐和高压锅炉的烟气中，Ｆｅ＿３Ａｌ的耐热腐蚀性能优于高温合金ＧＨ１３２．     

钢液定氧测头响应时间和热平衡态

本文分别研究了ＺｒＯ２（ＭｇＯ）固体电解质管头壁厚，参比电极量对定氧测头响应时间的影响，得出了以ＺｒＯ２管头壁厚为０．６０－０．８０ｍｍ，Ｃｒ／Ｃｒ２Ｏ３参比电极加入量为４０－６０ｍｇ所组成的定氧测头响应速度最快，同时采用了“双偶法”对定氧测头在工作过程中的热平衡态进行了研究。结果表明：氧浓差电池中的传热是响应过程的控速步骤，氧电势曲线上峰值的产生是起源于电池中的热平衡态。